F4BM-2-A Тефлоновый материал платы

F4BM-2-A: An Upgraded Version of the F4BM Series

Introduction to F4BM-2-A

F4BM-2-A is an enhanced iteration within the F4BM series, отличается от его превосходной электрической производительности и стабильности при сопротивлении поверхностной изоляции. It is constructed through a sophisticated process involving imported varnished glass cloth, Nano-ceramic membrane, and Teflon PCB resin, adhering to stringent technological standards.

Technical Specifications of F4BM-2-A

Внешний вид и типы

F4BM-2-A meets national and military standards for microwave PCB laminates. It comes in various types including F4BM-2-A255, F4BM-2-A262, F4BM-2-A275, F4BM-2-A285, F4BM-2-A294, and F4BM-2-A300.

Размеры

Available dimensions range from 550440мм до 15001000мм. Пользовательские размеры также доступны по запросу.

Толщина и толерантность

Laminate thicknesses vary from 0.254mm to 12.0mm, with specific tolerances ranging from ±0.025mm to ±0.2mm depending on the thickness.

Механическая прочность

• Сила резания/удара: Depending on thickness, there are no burrs after cutting, and the minimum space between punching holes varies to prevent delamination.
• Прочность на очистку: For a 1oz copper layer, normal state peel strength is ≥16N/cm; under constant humidity and temperature conditions, it is ≥12N/cm.

Химические свойства

The material allows for chemical etching without altering dielectric properties. Through-hole plating is possible but requires sodium or plasma treatment.

Электрические свойства

• Плотность: Ranges from 2.1 к 2.35 g/cm³ under normal conditions.
• Влажно -поглощение: Less than or equal to 0.07% after 24 hours in distilled water at 20±2°C.
• Рабочая температура: From -50°C to +260°C.
• Теплопроводность: Between 0.45~0.55 W/m/k.
• Коэффициент термического расширения (КТР): Varies with temperature and dielectric constant values.
• Shrinkage Factor: Less than or equal to 0.0002% after 2 hours in boiling water.
• Surface and Volume Resistivity: High resistivity under normal and constant humidity/temperature conditions.
• Dielectric Constant and Dissipation Factor: Stable across a range of frequencies with low dissipation factors.

Рейтинг воспламеняемости

Рейтинг воспламеняемости UL: 94В-0.

Заключение

F4BM-2-A represents a significant advancement in the F4BM series, offering improved electrical performance and mechanical stability, making it suitable for high-frequency applications where reliability and performance are paramount.